Research progress and prospective on processing techniques of all-ceramic restorations based on additive manufacturing

doi:10.3877/cma.j.issn.1674-1366.2020.02.001

Abstract

Abstract:

Compared with metal or metal-ceramic restorations, all-ceramic restorations embody eminent advantages, which have been widely applied in clinic. Characterized by equivalent manufacturing (EM) and subtractive manufacturing (SM) , traditional processing techniques of all-ceramic fixed dental prostheses (FDPs) have been well developed, but still remain defective. Rapid evolution of science and technology witnessed the changing of traditional manufacturing pattern of prosthetic dentistry (PD) with the emergency of additive manufacturing (AM) , which has been utilized by many scholars to fabricate all-ceramic FDPs. This review briefly stated the current condition of processing techniques of all-ceramic restorations and the theory and advantages of AM, meanwhile, emphasized the categories and research progress of AM based on ceramic materials for PD.

Key words: Additive manufacturing, Ceramics, Fixed dental prostheses

Yanze Cao, Hongbo Wei, Jiayi Dong, Rong Cai, Dehua Li. Research progress and prospective on processing techniques of all-ceramic restorations based on additive manufacturing[J]. Chinese Journal of Stomatological Research(Electronic Edition), 2020, 14(02): 65-70.

/ / Recommend

Add to citation manager EndNote|Ris|BibTeX

URL: https://zhkqyxyjzz.cma-cmc.com.cn/EN/10.3877/cma.j.issn.1674-1366.2020.02.001

https://zhkqyxyjzz.cma-cmc.com.cn/EN/Y2020/V14/I02/65

Figures/Tables 1

References 35

[1]	Butt K，Thanabalan N，Ayub K，et al. Demystifying Modern Dental Ceramics[J]. Prim Dent J，2019，8（3）：28-33. DOI：10.1308/205016819827601527.
[2]	周安亮，王德成，屈贤明.基于历史发展的等材制造智能化趋势研究[J].机电产品开发与创新，2018，31（2）：10-12. DOI：10.3969/j.issn.1002-6673.2018.02.004.
[3]	Lu B，Li D，Tian X. Development Trends in Additive Manufacturing and 3D Printing[J]. Engineering，2015，1（1）：85-89. DOI：10.15302/J-ENG-2015012.
[4]	赵信义.全锆冠桥修复热点问题浅析[J].口腔材料器械杂志，2018，27（1）：1-6. DOI：10.11752/j.kqcl.2018.01.01.
[5]	Rodrigues SB，Franken P，Celeste RK，et al. CAD/CAM or conventional ceramic materials restorations longevity：a systematic review and meta-analysis[J]. J Prosthodont Res，2019，63（4）：389-395.DOI：10.1016/j.jpor.2018.11.006.
[6]	Uçar Y，Aysan Meriç I，Ekren O. Layered Manufacturing of Dental Ceramics：Fracture Mechanics，Microstructure，and Elemental Composition of Lithography-Sintered Ceramic[J]. J Prosthodont，2019，28（1）：e310-e318. DOI：10.1111/jopr.12748.
[7]	Barazanchi A，Li KC，Al-Amleh B，et al. Additive Technology：Update on Current Materials and Applications in Dentistry[J]. J Prosthodont，2017，26（2）：156-163. DOI：10.1111/jopr.12510.
[8]	American Society for Testing Material（ASTM）. ASTM F2792-12 Standard Terminology for Additive Manufacturing Technologies[S]. DOI：10.1520/F2792-12.
[9]	Shah S，Ashok V，Ganapathy D. Comparative evaluation of rapid prototyping and computer-aided milling in prosthodontics - A review[J]. Drug Invention Today，2019，12（5）：1040-1043.
[10]	陈为平，林有希，黄捷，等. 3D打印发展现状分析及展望[J].工具技术，2019，53（8）：10-14. DOI：10.3969/j.issn.1000-7008.2019.08.002.
[11]	Ebert J，Ozkol E，Zeichner A，et al. Direct inkjet printing of dental prostheses made of zirconia[J]. J Dent Res，2009，88（7）：673-676. DOI：10.1177/0022034509339988.
[12]	Shahzad K，Deckers J，Zhang Z，et al. Additive manufacturing of zirconia parts by indirect selective laser sintering[J]. J Eur Ceram Soc，2014，34（1）：81-89. DOI：10.1016/j.jeurceramsoc.2013.07.023.
[13]	Wilkes J，Hagedorn YC，Meiners W，et al. Additive Manufacturing of ZrO2-Al2O3 Ceramic Components by Selective Laser Melting[J]. Rapid Prototyp J，2013，19（1）：51-53. DOI：10.1108/13552541311292736.
[14]	Lian Q，Sui W，Wu X，et al. Additive manufacturing of ZrO₂ ceramic dental bridges by stereolithography[J]. Rapid Prototyping J，2018，24（1）：114-119. DOI：10.1108/RPJ-09-2016-0144.
[15]	Dehurtevent M，Robberecht L，Hornez JC，et al. Stereolithography：A new method for processing dental ceramics by additive computer-aided manufacturing[J]. Dent Mater，2017，33（5）：477-485. DOI：10.1016/j.dental.2017.01.018.
[16]	Chen Z，Li Z，Li J，et al. 3D printing of ceramics：A review[J]. J Eur Ceram Soc，2019，39（4）：661-687. DOI：10.1016/j.jeurceramsoc.2018.11.013.
[17]	Lewis JA，Smay JE，Stuecker J，et al. Direct Ink Writing of Three Dimensional Ceramic Structures[J]. J Am Ceram Soc，2006，89（12）：3599-3609. DOI：10.1111/j.1551-2916.2006.01382.x.
[18]	Chia HN，Wu BM. Recent advances in 3D printing of biomaterials[J]. J Biol Eng，2015，9（1）：4. DOI：10.1186/s13036-015-0001-4.
[19]	纪宏超，张雪静，裴未迟，等.陶瓷3D打印技术及材料研究进展[J].材料工程，2018，46（7）：19-28. DOI：10.11868/j.issn.1001-4381.2018.000084.
[20]	Özkol E，Halloran J. Rheological Characterization of Aqueous 3Y-TZP Inks Optimized for Direct Thermal Ink-Jet Printing of Ceramic Components[J]. J Am Ceram Soc，2013，96（4）：1124-1130. DOI：10.1111/jace.12285.
[21]	Wei X，Li X，Wen S，et al. Channel design for 3D models with applications in powder-bed additive manufacturing[J]. Rapid Prototyp J，2019，25（9）：1536-1544. DOI：10.1108/RPJ-06-2018-0156.
[22]	李亚运，司云晖，熊信柏，等.陶瓷3D打印技术的研究与进展[J].硅酸盐学报，2017，45（6）：793-805. DOI：10.14062/j.issn.0454-5648.2017.06.07.
[23]	Shahzad K，Deckers J，Boury S，et al. Preparation and indirect selective laser sintering of alumina/PA microspheres[J]. Ceram Int，2012，38（2）：1241-1247. DOI：10.1016/j.ceramint.2011.08.055.
[24]	Sing SL，Yeong WY，Wiria FE，et al. Direct selective laser sintering and melting of ceramics：a review[J]. Rapid Prototyp J，2017，23（3）：611-623. DOI：10.1108/rpj-11-2015-0178.
[25]	Zheng Y，Zhang K，Liu TT，et al. Cracks of alumina ceramics by selective laser melting[J]. Ceram Int，2019，45（1）：175-184. DOI：10.1016/j.ceramint.2018.09.149.
[26]	Xing H，Zou B，Li S，et al. Study on surface quality，precision and mechanical properties of 3D printed ZrO₂ ceramic components by laser scanning stereolithography[J]. Ceram Int，2017，43（18）：16340-16347. DOI：10.1016/j.ceramint.2017.09.007.
[27]	Wang W，Yu H，Liu Y，et al. Trueness analysis of zirconia crowns fabricated with 3-dimensional printing[J]. J Prosthet Dent，2019，121（2）：285-291. DOI：10.1016/j.prosdent.2018.04.012.
[28]	Kim C，Kim S，Kim J，et al. Trueness of milled prostheses according to number of ball-end mill burs[J]. J Prosthet Dent，2016，115（5）：624-629. DOI：10.1016/j.prosdent.2015.10.014.
[29]	王文俊，钱超，阿地力江·依米提，等.立体光固化快速成型氧化锆全瓷冠的实验研究[J].口腔颌面修复学杂志，2018，19（5）：257-261. DOI：10.3969/j.issn.1009-3761.2018.05.002.
[30]	Aznarte Garcia E，Qureshi AJ，Ayranci C. A study on material-process interaction and optimization for VAT-photopolymerization processes[J]. Rapid Prototyp J，2018，24（9）：1479-1485. DOI：10.1108/RPJ-10-2017-0195.
[31]	Li H，Lu S，Sun J，et al. Dental ceramic prostheses by stereolithography-based additive manufacturing：potentials and challenges[J]. Adv Appl Ceram，2019，118（1-2）：30-36. DOI：10.1080/17436753.2018.1447834.
[32]	Lian Q，Wu X，Li D，et al. Accurate printing of a zirconia molar crown bridge using three-part auxiliary supports and ceramic mask projection stereolithography[J]. Ceram Int，2019，45（15）：18814-18822. DOI：10.1016/j.ceramint.2019.06.111.
[33]	周宏志，梁银生.一种用高粘度材料进行三维打印的随形制作方法：中国，CN109551758A[P]. 2019-04-02.
[34]	Cano S，Gonzalez-Gutierrez J，Sapkota J，et al. Additive manufacturing of zirconia parts by fused filament fabrication and solvent debinding：Selection of binder formulation[J]. Addit Manuf，2019，26：117-128. DOI：10.1016/j.addma.2019.01.001.
[35]	谢志鹏，许靖堃，安迪.先进陶瓷材料烧结新技术研究进展[J].中国材料进展，2019，38（9）：821-830. DOI：10.7502/j.issn.1674-3962.201906007.

技术分类	技术特点	技术优势	技术缺陷
直接喷墨打印（DIP）	经喷嘴喷射含粘接剂的陶瓷悬浮液	成品致密度较高，力学性能较好；材料利用率高；打印速度快；无支撑设计	悬浮液不稳定，喷嘴易堵塞，成型精度与质量难控制，成型周期有不确定性
选择性激光烧结（SLS）	CO₂激光烧结含粘接剂的陶瓷粉末	材料利用率高，选材广	成品致密度不足，表面质量差，工艺处理复杂
选择性激光熔化（SLM）	Nd：YAG激光直接熔化陶瓷粉末	成品致密度较高，材料利用率高，无需脱脂烧结	结构稳定性欠佳，表面质量差，工艺处理复杂
激光扫描式立体光刻（LSSL）	紫外激光点光源固化含光敏树脂的陶瓷浆料	成型精度与表面质量极佳，成品致密度与力学性能优良，材料利用率高	打印速度较慢，成型周期有不确定性
面曝光式立体光刻（MPSL）	紫外光LED面光源固化含光敏树脂的陶瓷浆料	打印速度较快，成品致密度与力学性能优良，材料利用率高	翘曲变形现象较为明显，成型精度与表面质量有待提高，成型周期有不确定性

技术分类	技术特点	技术优势	技术缺陷
直接喷墨打印（DIP）	经喷嘴喷射含粘接剂的陶瓷悬浮液	成品致密度较高，力学性能较好；材料利用率高；打印速度快；无支撑设计	悬浮液不稳定，喷嘴易堵塞，成型精度与质量难控制，成型周期有不确定性
选择性激光烧结（SLS）	CO₂激光烧结含粘接剂的陶瓷粉末	材料利用率高，选材广	成品致密度不足，表面质量差，工艺处理复杂
选择性激光熔化（SLM）	Nd：YAG激光直接熔化陶瓷粉末	成品致密度较高，材料利用率高，无需脱脂烧结	结构稳定性欠佳，表面质量差，工艺处理复杂
激光扫描式立体光刻（LSSL）	紫外激光点光源固化含光敏树脂的陶瓷浆料	成型精度与表面质量极佳，成品致密度与力学性能优良，材料利用率高	打印速度较慢，成型周期有不确定性
面曝光式立体光刻（MPSL）	紫外光LED面光源固化含光敏树脂的陶瓷浆料	打印速度较快，成品致密度与力学性能优良，材料利用率高	翘曲变形现象较为明显，成型精度与表面质量有待提高，成型周期有不确定性