Research on the synthesis and biocompatibility of the low-shrinkage resin root canal sealer

doi:10.3877/cma.j.issn.1674-1366.2010.06.002

Abstract

Abstract:

Objective

The aims of this study were to synthesize the low-shrinkage resin root canal sealer （LSRCS） based on the new monomer of bisphenol A glycidyl methacrylate and to evaluate the biocompatibility.

Methods

LSRCS was created by mixing organic monomer with special ratio and inorganic filler.The ratio and quantity of the inorganic filler were screened by the conversion， polymerization shrinkage， flow and solubility of the sealer.The biocompatibility was evaluated by the ISO 10993 of cytotoxicity， hemolysis assay， acute systemic toxicity and Guinea Pig Maximization Test.

Results

We synthesized the LSRCS with the inorganic ration of BaSO₄ ∶ZnO ∶HA equaling 9 ∶3 ∶2 and quantity percent of 50%.The cytotoxicity order of the three sealer was Epiphany＞LSRCS＞AH Plus.The KM mouse had no sharp difference between the experiment group and the control group in weight， activity， respiration and histopathologic appearance.The hemolysis ratio of LSRCS was 0.20% and no edema or erythema emerged on the experimental group in GPMT.

Conclusions

The new developed LSRCS has good biocompatibility.

Key words: Bisphenol A glycidyl methacrylate, Biocompatibility, Cytotoxicity, Root canal sealer, MTT, Hemolysis test, Guinea Pig Maximization Test

Jun-yan FANG, Zheng-mei LIN, Jun-qi LING, Jing-wei HE, Fang LIU, Yuan-fang LUO. Research on the synthesis and biocompatibility of the low-shrinkage resin root canal sealer[J]. Chinese Journal of Stomatological Research(Electronic Edition), 2010, 4(06): 540-547.

/ / Recommend

Add to citation manager EndNote|Ris|BibTeX

URL: https://zhkqyxyjzz.cma-cmc.com.cn/EN/10.3877/cma.j.issn.1674-1366.2010.06.002

https://zhkqyxyjzz.cma-cmc.com.cn/EN/Y2010/V4/I06/540

Figures/Tables 5

References 22

1	Nunes VH， Silva RG， Alfredo E， et al.Adhesion of Epiphany and AH Plus sealers to human root dentin treated with different solutions.Braz Dent J， 2008，19（1）：46-50.
2	Versiani MA， Carvalho-Junior JR， Padilha MI， et al.A comparative study of physicochemical properties of AH Plus and Epiphany root canal sealants.Int Endod J， 2006，39（6）：464-471.
3	Eldeniz AU， Mustafa K， Ørstavik D， et al.Cytotoxicity of new resin-， calcium hydroxide- and silicone-based root canal sealers on fibroblasts derived from human gingiva and L929 cell lines.Int Endod J， 2007，40（5）：329-337.
4	Susini G， About I， Tran-Hung L， et al.Cytotoxicity of Epiphany and Resilon with a root model.Int Endod J， 2006，39（12）：940-944.
5	Charton C， Falk V， Marchal P， et al.Influence of Tg， viscosity and chemical structure of monomers on shrinkage stress in light-cured dimethacrylate-based dental resins.Dent Mater， 2007，23（11）：1447-1459.
6	Key JE， Rahemtulla FG， Eleazer PD.Cytotoxicity of a new root canal filling material on human gingival fibroblasts.J Endod， 2006，32（8）：756-758.
7	Bouillaguet S， Shaw L， Barthelemy J， et al.Long-term sealing ability of Pulp Canal Sealer， AH-Plus， GuttaFlow and Epiphany.Int Endod J， 2008，41（3）：219-226.
8	Oddoni PG， Mello I， Coil JM， et al.Coronal and apical leakage analysis of two different root canal obturation systems.Braz Oral Res，2008，22（3）：211-215.
9	林正梅，凌均棨，刘芳，等.新型树脂根管充填材料的制备及其稳定性评价.中华口腔医学杂志， 2007，42（4）：235-239.
10	林正梅，凌均棨，刘芳，等.新型双甲基丙烯酸酯树脂根管封闭剂的制备与理化特性评价.中山大学学报（自然科学版）， 2007，46（2）：49-54.
11	Liu F， He JW， Lin ZM， et al.Synthesis and characterization of dimethacrylate monomer with high molecular weight for root canal filling materials.Molecules， 2006，11（12）：953-958.
12	Dahl JE， Frangou-Polyzois MJ， Polyzois GL.In vitro biocompatibility of denture relining materials.Gerodontology， 2006，23（1）：17-22.
13	中华人民共和国医药行业标准.YY/T 0127.1-1993 口腔材料生物试验方法：溶血试验.北京：中国标准出版社， 1993.
14	中华人民共和国国家标准.GB/T 16886.10-2005 医疗器械生物学评价，第10 部分：刺激与迟发型超敏反应试验.北京：中国标准出版社， 2005.
15	Halvorson RH， Erickson RL， Davidson CL.The effect of filler and silane content on conversion of resin-based composite.Dent Mater，2003，19（4）：327-333.
16	He J， Luo Y， Liu F， et al.Synthesis， characterization and photopolymerization of a new dimethacrylates monomer based on （alphamethybenzylidene） bisphenol used as root canal sealer.J Biomater Sci Polym Ed， 2010，21（8-9）：1191-1205.
17	Versiani MA， Carvalho-Junior JR， Padilha MI， et al.A comparative study of physicochemical properties of AH Plus and Epiphany root canal sealants.Int Endod J， 2006，39（6）：464-471.
18	中华人民共和国国家标准.GB/T 16886.5-2003 医疗器械生物学评价，第5 部分：体外细胞毒性试验.北京：中国标准出版社， 2003.
19	Oztan MD， Yilmaz S， Kalayci A， et al.A comparison of the in vitro cytotoxicity of two root canal sealers.J Oral Rehabil， 2003，30（4）：426-429.
20	Lodiene G， Morisbak E， Bruzell E， et al.Toxicity evaluation of root canal sealers in vitro.Int Endod J， 2008，41（1）：72-77.
21	中华人民共和国国家标准.GB/T 16886.11-1997 医疗器械生物学评价，第11 部分：全身毒性试验.北京：中国标准出版社， 1997.
22	Kleinsasser NH， Schmid K， Sassen AW， et al.Cytotoxic and genotoxic effects of resin monomers in human salivary gland tissue and lymphocytes as assessed by the single cell microgel electrophoresis （Comet） assay.Biomaterials， 2006，27（9）：1762-1770.

组别	BaSO₄（g）	ZnO（g）	HA（g）	流动性（mm）	溶解性（%）
1	3	1	1	22.28	2.25
2	3	2	2	23.48	2.11
3	3	3	3	22.07	2.54
4	6	1	2	21.79	2.83
5	6	2	3	20.02	3.97
6	6	3	1	20.95	1.81
7	9	1	3	19.61	3.41
8	9	2	1	19.35	1.10
9	9	3	2	20.96	0.76

组别	BaSO₄（g）	ZnO（g）	HA（g）	流动性（mm）	溶解性（%）
1	3	1	1	22.28	2.25
2	3	2	2	23.48	2.11
3	3	3	3	22.07	2.54
4	6	1	2	21.79	2.83
5	6	2	3	20.02	3.97
6	6	3	1	20.95	1.81
7	9	1	3	19.61	3.41
8	9	2	1	19.35	1.10
9	9	3	2	20.96	0.76

填料含量	双键转化率（%）	聚合收缩（%）	流动性（mm）	溶解性（%）
50%	64.6±4.3	1.83	23.7±0.3	0.66±0.06
55%	58.7±4.5	1.61	21.7±0.7	0.69±0.04
60%	56.7±2.1	1.46	20.9±1.4	0.76±0.02
65%	47.6±2.2	1.39	19.6±0.8	0.79±0.04

填料含量	双键转化率（%）	聚合收缩（%）	流动性（mm）	溶解性（%）
50%	64.6±4.3	1.83	23.7±0.3	0.66±0.06
55%	58.7±4.5	1.61	21.7±0.7	0.69±0.04
60%	56.7±2.1	1.46	20.9±1.4	0.76±0.02
65%	47.6±2.2	1.39	19.6±0.8	0.79±0.04

封闭剂	24 h		48 h		72 h
封闭剂	RGR（%）	CG	RGR（%）	CG	RGR（%）	CG
LSRCS	1.0468	无	0.9779	无	0.7838	轻
Epiphany	0.6022	轻	0.4684	中	0.3395	中
AH Plus	1.0293	无	1.0740	无	0.9342	无